Semiconductor device and method of manufacturing the same

ABSTRACT

A hard mask  105  of SiCN is formed on a fluorine-containing carbon film  103.  Thus, the adhesion of the hard mask  105  to the fluorine-containing carbon  103  is improved and inhibited from being peeled off. The hard mask  105  of SiCN can have a higher etch-selectivity than those of conventional hard masks, and can have a lower dielectric constant than that of SiN or SiC.

TECHNICAL FIELD

[0001] The present invention relates to a semiconductor device, which uses a carbon-containing layer, such as a fluorine-containing carbon film, as an insulating film, and a method of manufacturing the same.

BACKGROUND ART

[0002] In order to achieve the high-density integration of semiconductor integrated circuits, it has been developed to scale down patterns, such as wiring, and to multilayer circuits. As one of such developments, there is a multi-layer metallization technique for constructing multi-layer wiring. In this multi-layer metallization technique, upper and lower wiring layers are connected to each other by a conductive part which is arranged in a predetermined region, and an interlayer dielectric film of an insulating material is arranged to separate the wiring layers from each other in a region other than the conductive part.

[0003] Typical materials of the interlayer dielectric films include silicon oxide (SiO₂). In recent years, in order to more accelerate the operation of integrated circuits, it has been required to lower the relative dielectric constant of the interlayer dielectric films. That is, the relative dielectric constant ε of SiO₂ is about 4, and materials having a lower relative dielectric constant than that of SiO₂ have been diligently developed.

[0004] As an example of a material having a lower relative dielectric constant than that of SiO₂, there is a fluorine-containing carbon film comprising carbon and fluorine. This fluorine-containing carbon film can be formed by, e.g., a plasma deposition process using the electron cyclotron resonance (ECR). This method will be described below.

[0005] In a deposition system shown in FIG. 9, a microwave of 2.45 GHz is first supplied into a plasma producing chamber 801 a from a high-frequency power supply part 802 via a waveguide 802 a. At this time, a magnetic field of 875 gausses is applied by magnetic coils 803 and 803 a, and Ar gas introduced from an introducing pipe 804 is activated as a high-density plasma by the electron cyclotron resonance.

[0006] On the other hand, C₄F₅ gas and C₂H₄ gas are introduced into a deposition chamber 801 b from a gas supply part 805 via gas introducing pipes 805 a and 805 b to be activated by the high-density plasma to form active-species. By the active-species, a fluorine-containing carbon film 808 having good adhesion and high hardness is formed on the surface of a wafer 807 which is arranged on a supporting table 806 in the deposition chamber 801 b. The wafer 807 is fixed by an electrostatic chuck 806 a on the supporting table 806. The interior of the deposition chamber 801 b is evacuated to a predetermined degree of vacuum by an evacuating means (not shown) which is communicated with the deposition chamber 801 b via an exhaust pipe 810.

[0007] By the foregoing, the fluorine-containing carbon film can be formed. However, in order to use the fluorine-containing carbon film as an interlayer dielectric film, it is required to carry out a fine patterning process, such as the formation of a hole portion for arranging a connecting portion for connecting upper and lower wiring layers to each other.

[0008] The fine patterning process of the fluorine-containing carbon film will be described below. First, as shown in FIG. 11(a), a fluorine-containing carbon film 902 is formed on a lower wiring layer 901 serving as a substrate as described above. On the fluorine-containing carbon film 902, an inorganic film 903 of SiO₂ is formed. Then, as shown in FIG. 11(b), a resist pattern 904 having an opening 904 a at a predetermined place is formed on the inorganic film 903 by a well-known photolithography technique.

[0009] The resist pattern 904 is then used as a mask to selectively etch the inorganic film 903. Thus, as shown in FIG. 11(c), a hard mask 905 having an opening 905 a at a position corresponding to the opening 904 a is formed. This etching may be, e.g., a dry etching with the plasma of CF₄.

[0010] The hard mask 905 is then used as a mask to selectively etch the fluorine-containing carbon film 902. Thus, as shown in FIG. 11(d), a hole portion 906 is formed in the fluorine-containing carbon film 902. This etching may be, e.g., a dry etching with the plasma of oxygen gas. If oxygen gas is used, the etch-selectivity (the ratio of etch rates) between the fluorine-containing carbon film 902 and the hard mask 905 can be great. If the plasma of oxygen gas is used, the resist pattern 904 can be simultaneously removed.

[0011] The fine patterning process of the fluorine-containing carbon film using the hard mask will be described below.

[0012] In the fine patterning process, a resist pattern formed by the photolithography technique is generally used as a mask to selectively etch. At this time, the resist pattern must have an etching resistance as a mask for an underlying layer to be processed. When the layer to be processed is thick, the resist pattern must particularly have the etching resistance. This resist pattern is formed by, e.g., exposing and developing a photoresist having photosensitivity, and made of an organic material.

[0013] However, when an organic film, such as the above described fluorine-containing carbon film, is fine-patterned, the dry etching with the plasma of oxygen is used. In this case, if a resist pattern of an organic film is used as a mask, the resist pattern is also etched, so that it is not possible to carry out a selective etching.

[0014] On the other hand, if a master pattern of an inorganic material, such as SiO₂, is used when the fluorine-containing carbon film is etched with the plasma of oxygen gas, the master pattern is hardly etched with the plasma of oxygen, so that it is possible to carry out a selective etching For that reason, as described above, a hard mask of SiO₂ or the like is used for fine-patterning the fluorine-containing carbon film.

[0015] By the way, in order to form this hard mask, an inorganic film of SiO₂ or the like is patterned. This patterning may use a dry etching with the plasma of CF₄ or C₄F₅. In this case, since the resist pattern of the organic film is hardly etched, the resist pattern can be used as a mask to carry out the selective etching to form the hard mask as described above.

[0016] However, if a hard mask of SiO₂ or silicon nitride (SiN), which are generally used for patterning organic films, is used for fine-patterning the fluorine-containing carbon film, there are the following problems, so that the reliability of semiconductor devices using a fluorine-containing carbon film as an interlayer film is deteriorated.

[0017] First, since SiO₂ and SiN have low adhesion to the fluorine-containing carbon film which is a fluorine-containing organic film, there is a problem in that the hard mask is easily peeled off. As described above, since the hard mask is made of the insulating material, the hard mask is used as a part of an interlayer dielectric film. However, after the fluorine-containing carbon film serving as the interlayer dielectric film is fine-patterned, if a stress is applied in the subsequent process such as forming a metal film for a wiring electrode thereon, the hard mask is sometimes peeled off. If the metal film for the wiring electrode is intended to be flattened by the chemical mechanical polishing method after the metal film is formed, a great stress is applied thereto, so that the hard mask is substantially surely peeled off from the fluorine-containing carbon film.

[0018] Next, if the hard mask of SiO₂ or SiN is used for fine-patterning the fluorine-containing carbon film, there is a problem in that the etch-selectivity is lowered as follows. As described above, the dry etching with the plasma of oxygen gas is used for fine-patterning the fluorine-containing carbon film. In view of only this point, a high etch-selectivity should be obtained if the hard mask is made of SiO₂ or SiN.

[0019] However, when the fluorine-containing carbon film is etched with the plasma of oxygen gas, the fluorine-containing carbon film is decomposed to produce F (fluorine) and C (carbon) in atmosphere, and the active-species of F and C are produced by plasma. As a result, since SiO₂ or SiN is etched with the active-species, there is a problem in that if the conventional hard mask, together with the fluorine-containing carbon film, is etched, the etch-selectivity is lowered to deteriorate processing precision.

[0020] From the point of view of the acceleration of semiconductor devices, it is desired that the insulating film used as the hard mask is made of a material having a lower relative dielectric constant similar to the insulating film of the fluorine-containing carbon film.

DISCLOSURE OF THE INVENTION

[0021] The present invention has been made in order to eliminate the above described problems. That is, it is an object of the present invention to improve the reliability of a semiconductor device, which has a carbon-containing insulating film, such as a fluorine-containing carbon film, while considering the acceleration of the same.

[0022] In order to accomplish this object, according to one aspect of the present invention, a semiconductor device is provided, the device comprising: a semiconductor substrate, on which an active region is formed; a plurality of wiring layers which are formed on the semiconductor substrate; a first insulating layer containing carbon, the first insulating layer being formed at least between any adjacent two of the wiring layers; and a second insulating layer comprising silicon, carbon and nitrogen, the second insulating layer being formed on the first insulating layer.

[0023] With this construction, the first insulating layer containing carbon contacts the second insulating layer comprising silicon, carbon and nitrogen, so that the adhesion between the first and second insulating layers is improved to inhibit peeling. The second insulating layer comprising silicon, carbon and nitrogen can have a higher etch-selectivity than those of conventional layers, and can have a lower dielectric constant than that of an insulating layer comprising silicon and nitrogen or an insulating layer comprising silicon and carbon. Therefore, it is possible to improve the reliability of the semiconductor device while considering the acceleration of the same.

[0024] In such a semiconductor device, the second insulating layer preferably further comprises boron in order to lower the relative dielectric constant of the second insulating layer.

[0025] An adhesion layer comprising a high-melting point metal and a nitride thereof may be provided in the interface between the first insulating layer and the wiring layers.

[0026] According to another aspect of the present invention, a method of manufacturing a semiconductor device is provided, the method comprising the steps of: forming a wiring layer on a semiconductor substrate, on which an active region is formed; forming a first insulating layer containing carbon on the wiring layer; forming a second insulating layer comprising silicon, carbon and nitrogen on the first insulating layer; selectively etching the second insulating layer until the surface of the first insulating layer is partially exposed; selectively etching the first insulating layer using the selectively-etched, second insulating layer, as a mask; and forming a new wiring layer on the second insulating layer after selectively etching the first insulating layer.

[0027] With this construction, it is possible to obtain a semiconductor device wherein the first insulating layer containing carbon contacts the second insulating layer comprising silicon, carbon and nitrogen, between the wiring layers. Thus, the adhesion between the first and second insulating layers is improved to inhibit peeling. The second insulating layer comprising silicon, carbon and nitrogen, can have a higher etch-selectivity than those of conventional layers, and can have a lower dielectric constant than that of an insulating layer comprising silicon and nitrogen or an insulating layer comprising silicon and carbon. Therefore, it is possible to improve the reliability of the semiconductor device while considering the acceleration of the same.

[0028] This producing method preferably further comprises a step of adding boron to the second insulating layer in order to lower the relative dielectric constant of the second insulating layer.

[0029] The step of selectively etching the second insulating layer may be carried out with the plasma of the gas of a compound containing carbon and fluorine or with the plasma of the gas of a compound containing carbon and hydrogen.

[0030] If the step of selectively etching the first insulating layer is carried out with the plasma of an oxygen-containing gas, the second insulating layer and the wiring layers are hardly etched.

[0031] If the step of selectively etching the first insulating layer is carried out with the plasma of a hydrogen-containing gas, the step is controlled by the etching with reactive ions, so that it is possible to carry out a higher anisotropic etching.

BRIEF DESCRIPTION OF THE DRAWINGS

[0032]FIG. 1a is a local longitudinal section showing the structure of a preferred embodiment of a semiconductor device according to the present invention;

[0033]FIG. 1b is an enlarged view showing a part of the structure shown in FIG. 1a;

[0034]FIG. 2 is a schematic longitudinal section showing steps (a) through (h) of a preferred embodiment of a method of manufacturing a semiconductor device according to the present invention;

[0035]FIG. 3 is a schematic longitudinal section for explaining a method for measuring adhesive strength;

[0036]FIG. 4 is a graph showing the difference between the adhesive strengths of hard mask materials;

[0037]FIG. 5 is a graph showing the difference between the adhesive strengths of underlying films to a hard mask;

[0038]FIG. 6 is a graph showing the difference between the relative dielectric constants of hard mask materials;

[0039]FIG. 7 is a graph showing the difference between the relative dielectric constants of boron-containing hard mask materials;

[0040]FIG. 8 is a graph showing the difference in relative dielectric constant of a hard mask in processes;

[0041]FIG. 9 is a local longitudinal section showing the structure of another preferred embodiment of a semiconductor device according to the present invention;

[0042]FIG. 10 is a schematic longitudinal section showing the structure of a plasma deposition system for forming a fluorine-containing carbon film; and

[0043]FIG. 11 is a schematic longitudinal section showing steps (a) through (d) of a conventional method of manufacturing a semiconductor device.

BEST MODE FOR CARRYING OUT THE INVENTION

[0044] Referring to drawings, the preferred embodiments of the present invention will be described below.

First Preferred Embodiment

[0045] First, a semiconductor device serving as the first preferred embodiment of the present invention will be described. In this preferred embodiment, a semiconductor device is constructed as shown in FIG. 1a. This construction will be described. An insulating film 101, e.g., an SiO₂ film, is formed so as to cover an active region (not shown), such as a MOS transistor, which is formed on a semiconductor substrate of silicon (Si). A wiring layer (not shown) of, e.g., W, which is electrically connected to the active region, and a wiring layer 102 of, e.g., copper (Cu), connected to the wiring layer are formed on the insulating film 101.

[0046] On the SiO₂ film 101, a fluorine-containing carbon film 103 serving as a first insulating film is formed so as to cover the Cu layer 102. In the fluorine-containing carbon film 103, a groove portion 104 a and a hole portion 104 b are formed. In the groove portion 104 a and the hole portion 104 b, a wiring layer 104 of, e.g., Cu, is formed. The wiring layer 104 is electrically connected to the Cu layer 102. Between the contact surfaces of the Cu layer 104 and the fluorine-containing carbon film 103, and between the contact surface of the Cu layer 104 and the Cu layer 102, an adhesion layer 104 c is formed.

[0047] In order to improve the adhesion of the Cu layer 104 to the fluorine-containing carbon film 103, the adhesion layer 104 c comprises, e.g., a TiN layer 104 c′ and a Ti layer 104 c″ as shown in FIG. 1b. The structure of the adhesion layer 104 c should not be limited to such a TiN/Ti stacked structure, but it may be another stacked structure of a high-melting point metal nitride and a high-melting point metal, such as TaN/Ta or WN/W.

[0048] In the first preferred embodiment, a hard mask 105 of SiCN serving as a second insulating film having a thickness of about 100 nm is formed on the fluorine-containing carbon film 103. The SiCN does not always mean a chemical composition or a chemical bonding structure, but it means to include Si, C and N as components.

[0049] On the hard mask 105, a fluorine-containing carbon film 106 serving as a first insulating layer, a Cu layer 107 embedded in a groove portion 107 a and a hole portion 107 b, an adhesion layer 107 c, and a hard mask 108 of SiCN are formed so as to have the same structure as that described above. That is, the hard mask 108 of SiCN is also formed on the fluorine-containing carbon film 106 so as to have a thickness of about 100 nm. Since the Cu layer 104 and the Cu layer 107 are made of the same material, it is not required to form any barrier films on the contact interface therebetween.

[0050] As described above, in this first preferred embodiment, the hard masks 105 and 108 are provided on the interlayer dielectric films 103 and 106 of the fluorine-containing carbon films. As a result, for example, the hard mask 105 of SiCN is arranged between the fluorine-containing carbon film 103 and the fluorine-containing carbon films 106, so that the adhesion between the respective layers 103, 105 and 106 can be more improved than conventional devices using a hard mask of SiO₂.

[0051] On the hard mask 108 and the Cu layer 107, the same stacked structure may be provided to form a semiconductor device. That is, an optional number of stages of the same stacked structures may be stacked to form a semiconductor device.

[0052] A method of manufacturing the above described wiring structure will be described below. Steps after the formation of the Cu layer 104 and the hard mask 105 will be described.

[0053] First, as shown in FIG. 2(a), a fluorine-containing carbon film 206 having a thickness of about 700 nm is formed on the Cu layer 104 and the hard mask 105 of SiCN. As described above, the fluorine-containing carbon film 206 is formed by a plasma deposition process using the electron cyclotron resonance (ECR) using C₄F₅ gas and C₂H₄ gas as raw material gases.

[0054] Then, as shown in FIG. 2(b), an insulating film 208 of SiCN is formed on the fluorine-containing carbon film 206. This may be formed by the chemical vapor deposition (CVD) method using, e.g., SiH₄, C₂H₄ and N₂ as raw material gases. On the insulating film 208, a resist pattern 211 having a hole portion 211 a at a predetermined place is formed. The resist pattern 211 may be formed by a well-known photolithography technique.

[0055] The resist pattern 211 is then used as a mask to etch the insulating film 208 to form a hard mask 108 having a hole portion 208 a as shown in FIG. 2(c). This etching may use, e.g., a dry etching with the plasma of C₄F₅.

[0056] The hard mask 108 having the hole portion 208 a is then used as a mask to etch the underlying fluorine-containing carbon film 206. This etching may be a reactive ion etching with the plasma of oxygen gas. Since the hard mask 108 is made of SiCN as described above, the hard mask 108 is hardly etched with the plasma of oxygen gas. On the other hand, the fluorine-containing carbon film 206 is etched (ashed) with the plasma of oxygen gas. By this etching process, a hole portion 206 a can be formed in the fluorine-containing carbon film 206 as shown in FIG. 2(d). Since the plasma of oxygen gas is used at this time, the resist pattern 211 of the organic film is simultaneously removed.

[0057] The etch-selectivity of the fluorine-containing carbon film and the hard mask of SiCN in the dry etching using the plasma of oxygen gas will be described. When hard mask materials, such as SiO₂ and SiN, together with the fluorine-containing carbon film, are dry-etched with the plasma of oxygen gas, etch rates (nm/min.) are shown as follows. Fluorine-containing 1538 carbon film SiN 37 SiC 45 SiO₂ 42 SiCN 15

[0058] As shown above, when each of the hard materials is processed simultaneously with the fluorine-containing carbon film, the etch rate of SiCN with the plasma of oxygen gas is a far smaller than those of other hard mask materials. Therefore, if the hard mask of SiCN is used as this first preferred embodiment, it is possible to obtain a high etch-selectivity in the etching for the fluorine-containing carbon film, so that it is possible to more improve processing precision.

[0059] Then, as shown in FIG. 2(e), a resist pattern 212 having a groove portion 212 a is formed on the hard mask 108. The resist pattern 212 may be formed by a well-known photolithography technique. The groove portion 212 a is formed so as to overlap with the hole portion 206 a.

[0060] The resist pattern 212 is then used as a mask to etch the hard mask 208 to form a groove 108 a in the hard mask 108. This etching may be, e.g., a dry etching with the plasma of C₄F₅. Since the fluorine-containing carbon film 206 is hardly etched by the dry etching with the plasma C₄F₅, the hard mask 108 can be selectively etched.

[0061] The hard mask 108 having the groove portion 108 a is then used as a mask to etch the fluorine-containing carbon film 206 to form a fluorine-containing carbon film 106 formed with a groove portion 107 a having a depth of about 400 nm as shown in FIG. 2(f). At this step, a reactive ion etching with the plasma of oxygen gas may be used. Since the plasma of oxygen gas is used, the resist pattern 212 on the hard mask 108 is simultaneously removed. Then, a through-hole 107 b based on the hole portion 206 a, which has been formed in the fluorine-containing carbon film 206, is arranged in a region in which the groove portion 107 a of the fluorine-containing carbon film 106 intends to be formed.

[0062] Then, as shown in FIG. 2(g), a thin metal film 207 a, which is an adhesion layer of a TiN layer and a Ti layer, is formed so as to cover the hard mask 108 and the surfaces of the through-hole 107 b and groove portions 107 a and 108 a. A metal film 207 of copper is then formed on the hard mask 108 via the metal film 207 a so as to be filled in the through-hole 107 b and the groove portions 107 a and 108 a. The metal film 207 may be formed by, e.g., a well-known metal film forming method, such as an electroless plating or a sputtering method.

[0063] The metal films 207 and 207 a are then polished from the surface by the chemical mechanical polishing (CMP). If the surface of the hard mask 108 is thus exposed as shown in FIG. 2(h), the Cu layer 107 is arranged on the Cu layer 104 via the fluorine-containing carbon film 106, and the fluorine-containing carbon film 106 and the Cu layer 107 contact each other via the adhesion layer 107 c having the TiN/Ti structure. Of course, the steps of forming the fluorine-containing carbon film 103 through the Cu layer 104 can be carried out substantially in the same manner although the descriptions of these steps are omitted.

[0064] The adhesions of the above described hard mask material of SiCN and a conventional hard mask material of SiO₂ to a fluorine-containing carbon film stacked thereto were compared with each other. In this case, the adhesive strengths in a triple layer structure of “fluorine-containing carbon film/hard mask/fluorine-containing carbon film” were compared with each other. As a reference, a hard mask material of SiN was examined.

[0065] The adhesive strengths are measured as follows. First, as shown in FIG. 3, a fluorine-containing carbon film 602, a hard mask 603 and a fluorine-containing carbon film 604 are sequentially stacked on a substrate 601 to prepare a sample, and a test rod 605 is fixed to the fluorine-containing carbon film 604 by a predetermined adhesive. A load is then applied to the test rod 605 so that the test rod 605 goes away from the substrate while the substrate 601 is fixed. It is assumed that the adhesive strength is a load (Kpsi) applied when any one of the films is peeled off.

[0066] The measured results of the above described adhesive strengths are shown in FIG. 4. As can be seen from FIG. 4, the adhesive strength to the fluorine-containing carbon film is remarkably improved by using SiCN as the material of the hard mask. When an adhesive strength of 5 Kpsi or more is thus obtained between the hard mask and the fluorine-containing carbon film, even if the hard mask remains as a part of the interlayer film, the hard mask is inhibited from being peeled off by the chemical mechanical polishing during the formation of the electrode (wiring layer).

[0067] The difference between the adhesive strengths of three kinds of underlying films A, B and C to a hard mask of SiCN was examined. The results thereof are shown in the graph of FIG. 5. In this case, the underlying film A is the above described fluorine-containing carbon film, the underlying film B is a “SiCO(H) film, where (H) is H in a C_(x)H_(y) group”, and the underlying film C is an SOD (Spin On Dielectric) film. The method for measuring the adhesive strength is the same as the above described method. The SiCO(H) film is formed by the plasma CVD method using, e.g., methylsilane which is expressed by SiH_(x)(CH₃)_(y), or an alkoxysilane as a raw material, alone or with oxygen-containing gas (O₂, N₂O, etc.). In this case, the SOD film is made of SiLK which is an organic polymer.

[0068] As described above, the hard mask is used as a part of an interlayer dielectric film between wiring layers. Therefore, even if the hard mask is thinner than the fluorine-containing carbon film, it is desirable that its dielectric constant is as small as possible. Therefore, comparing the relative dielectric constants ε of various hard mask materials with each other as shown in the graph of FIG. 6, the relative dielectric constant ε of SiCN in this preferred embodiment is about 5.5 which is far lower than about ε of SiN or SiC although it is higher than about 4 of SiO₂.

Second Preferred Embodiment

[0069] The second preferred embodiment of the present invention will be described. In the second preferred embodiment, boron (B) is added to a hard mask of SiCN in order to further lower the dielectric constant of the hard mask material for the above described reason. Although the relative dielectric constant ε of SiCN itself is about 5.5 as described above, the dielectric constant ε can be lowered to about 5.1 if boron is added to SiCN. Other constructions are the same as those in the above described first preferred embodiment.

[0070] In order to add boron, BF₃ may be used in addition to SiH₄, C₂H₄ and N₂ as raw material gases in the chemical vapor deposition method during the formation of the insulating film 208 of SiCN shown in, e.g., FIG. 2(b). As a combination of raw material gases, a combination of SiH₄, C₂H₄ and BF₃, or a combination of SiH₄, BF₃ and N₂ may be used. In place of BF₃, B₂F₆ may be used. Thus, the insulating film is formed of boron-containing SiCN, SiC or SiN (SiBCN, SiBC or SiBN).

[0071] The addition of boron may be carried out by the ion implantation into the insulating film already deposited.

[0072] The variation in relative dielectric constant was examined when boron was added to SiN, SiC and SiCN. The results thereof are shown in the graph of FIG. 7. As shown in FIG. 7, although the relative dielectric constants ε of SiN, SiC and SiCN are about 8.2, 7.9 and 5.5, respectively, the relative dielectric constants ε of SiBN, SiBC and SiBCN, which are formed by adding boron thereto, are lowered to be about 5.9, 5.5 and 5.1, respectively.

Other Preferred Embodiments

[0073] While the hard mask of SiCN has been formed by the process using “SiH₄+C₂H₄+N₂” as raw material gases in the above described preferred embodiments, the hard mask may be formed by a process using other raw material gases.

[0074] Hard masks of SiCN were formed by different three kinds of processes (raw materials) A, B and C, and the difference between relative dielectric constants of the hard masks of SiCN was examined. The results thereof are shown in the graph of FIG. 8. In this case, the process A uses “SiH₄+(a carbon-containing raw material gas)+(a nitrogen-containing raw material gas)” as raw material gases, similar to the above described process. In the processes B and C, SiH₄ in the process A is replaced with SiH_(x)(CH₃)_(y) and an alkoxysilane, respectively, to be used as raw material gases.

[0075] The carbon-containing raw material gas may be CH₄, C₂H₄, C₃H₆ or C₂H₂ other than the above described C₂H₄. The nitrogen-containing raw material gas may be NF₃, N₂O, NO₂, N₂O₄, NO or NH₄ other than the above described N₂.

[0076] As shown in FIG. 8, although the relative dielectric constant ε is about 5.5 in the process A which is used in the above described preferred embodiment, the relative dielectric constants ε in the processes B and C are lowered to be about 4.2 to 4.3. That is, according to the above described processes B and C, the relative dielectric constant can be further lowered as compared with that in the above described second preferred embodiment that boron is added.

[0077] While the plasma of oxygen gas has been used for etching the fluorine-containing carbon film, the plasma of a mixed gas of hydrogen gas, argon gas and nitrogen gas may be used. In this case, the flow ratio of argon gas to the mixed gas (Ar/(N₂+H₂+Ar)) may be substantially about 0.7 to about 0.8. The flow ratio of hydrogen gas to nitrogen gas (H₂/(N₂+H₂)) may be substantially 0.2 to 0.9. The degree of vacuum in plasma producing atmosphere may be about 5 mTorr to about 15 mTorr.

[0078] Also in this case, when the hard mask material is processed simultaneously with the fluorine-containing carbon film similar to when oxygen gas is used, the etch rate (nm/min.) of the hard mask material of SiCN is far smaller than those of other hard mask materials. Fluorine-containing 1826 carbon film SiN 58 SiC 88 SiO₂ 95 SiCN 18

[0079] The feature of the above described use of hydrogen gas for etching will be described. When the reactive ion etching with the plasma of hydrogen gas, argon gas and nitrogen gas is used for etching the fluorine-containing carbon film, the anisotropy of etching can be higher than that when oxygen gas is used.

[0080] It is considered that reactive ions and radicals are produced as etching active-species by producing plasma in dry etching processes. In a reactive ion etching, an electric field is utilized for mainly flying reactant ions to an object to be etched, the process is carried out in a high vertical anisotropic state.

[0081] However, since plasma is produced in atmosphere, radicals, which have not been attracted by the electric field, finally reach the object to be etched, to participate in the etching reaction. If the etching reaction due to the radicals occurs, a side etching, by which regions underlying the master pattern are etched, occurs. In such a mechanism, in the reactive ion etching with the plasma of oxygen gas, oxygen radicals have a high reactivity with respect to organic compounds, so that the oxygen radicals excessively participate in the etching reaction to lower the controllability of the etched shape of the fluorine-containing carbon film.

[0082] On the other hand, when the above described mixed gas of hydrogen gas, argon gas and nitrogen gas is used, the etching active-species against the fluorine-containing carbon film mainly become reactive hydrogen ions and radicals. However, hydrogen radicals do not have so high reactivity with respect to organic compounds. For that reason, in the case of the reactive ion etching using the mixed gas, the etching active-species against the fluorine-containing carbon film are substantially only reactive hydrogen ions. That is, in this case, the etching hardly proceeds by radicals having no directionality.

[0083] As a result, when the mixed gas of hydrogen gas, argon gas and nitrogen gas is used, a higher anisotropy is obtained to inhibit the side etching and so forth, so that it is possible to improve processing precision, such as directional controllability.

[0084] While the groove has been formed in the interlayer film of the fluorine-containing carbon film to be filled with the wiring layer in the above described preferred embodiments, the present invention should not be limited thereto. For example, a structure shown in FIG. 9 may be provided. In this structure, a hard mask 702 of SiCN is formed on an interlayer dielectric film 701 of a fluorine-containing carbon film, and a wiring layer 703 is formed thereon. The wiring layer 703 is connected to an underlying wiring layer (not shown) via a through-hole which is formed in the interlayer dielectric layer 701 and hard mask 702.

[0085] On the hard mask 702, an interlayer dielectric film 704 of a fluorine-containing carbon film is formed so as to cover the wiring layer 703. A hard mask 705 of SiCN is formed on the interlayer dielectric film 704, and a wiring layer 706 is formed thereon. The wiring layer 706 is connected to an underlying wiring layer 703 via a through-hole which is formed in the interlayer dielectric film 704 and hard mask 705.

[0086] In this case, the hard masks 702 and 705 are used for forming the through-holes for connecting the wiring layers to each other. Therefore, in this case, one fine patterning process is carried out for, e.g., the hard mask 705 and the interlayer dielectric film 704. However, for example, the wiring layer 706 is formed by forming a metal film on the hard mask 705 and by fine-patterning the metal film by well-known photolithography and etching techniques.

[0087] While the wiring layer has been made of Cu in the above described preferred embodiments, the present invention should not be limited thereto, but the wiring layer may be made of any one of other conductive materials, such as aluminum (Al). 

1. A semiconductor device comprising: a semiconductor substrate, on which an active region is formed; a plurality of wiring layers which are formed on said semiconductor substrate; a first insulating layer containing carbon, said first insulating layer being formed at least between any adjacent two of said wiring layers; and a second insulating layer comprising silicon, carbon and nitrogen, said second insulating layer being formed on said first insulating layer.
 2. A semiconductor device as set forth in claim 1, wherein said second insulating layer further comprises boron.
 3. A semiconductor device as set forth in claim 1, which further comprises an adhesion layer which comprises a high-melting point metal and a nitride thereof, said adhesion layer being formed in the interface between said first insulating layer and said wiring layers. 4-9. (Cancelled).
 10. A semiconductor device as set forth in claim 2, which further comprises an adhesion layer which comprises a high-melting point metal and a nitride thereof, said adhesion layer being formed in the interface between said first insulating layer and said wiring layers. 